• Low solubility
• Low film thickness
• Excellent abrasion resistance.
• High compressive & tensile strength.
• High strength comparable to zinc phosphate cement.
• Excellent physical properties due to added unique polymer reinforcing agents.

Zinconol is a polymer reinforced zinc oxide eugenol cement for temporary restoration. The
excellent physical properties resulting from the unique polymer reinforcing agents include high
compressive and tensile strength, excellent abrasion resistance and low solubility. Its strength
is comparable to Zinc Phosphate Cement.

Zinconol is a Eugenol based compositions and therefore it should not be used as a liner under resin based filling materials.

INDICATION :

• Sealing coronal portion of teeth under endodontics treatment
• As a base under amalgam and non-resin restorations
• Temporary restoration in emergency treatments
• Intermediate Restorative Material (IRM) for class I and class II restorations

Technical Data :

• Mixing time : 45- 60 seconds to a putty consistency.
• Working time : 2 min – 30 sec
• Setting time : 4-6 minutes
• Compressive Strength : 35MPa

Powder liquid ratio – 1 : 2 (2 scoop powder and 2-3 drops liquid.)

Composition :
Powder contains Zinc Oxide, Poly Methy Methacrylate Polymer and Zinc Acetate.
Liquid contains Eugenol.

Storage Condition : Store at temperature between 10°C to 24°C. Close the cap carefully after use. Keep away from moisture. Shelf life not affected after opening if stored in a cool dry place.

Shelf Life : 3 years from the date of manufacturing.

Powder-Liquid Kit

• 1 x Powder Jar 15g
• 1 x Liquid Bottle 10ml
• 1 x Mixing Pad
• 1 x Spoon
• 1 X Dispensing Dropper
• 1 x Instruction Manual

• Shake the bottle of powder well before use to ensure that the density is homogeneous.
• Powder and liquid should be mixed in proper ratio.
• Powder liquid ratio is 1 : 2 (2 scoop powder and 2-3 drops liquid.)
• Mixing should be completed in 45- 60 seconds to a putty consistency.
• Insert into the cavity and allow 4-6 minutes for proper hardening.